Glow of a foundry crucible

A foundry is a factory that produces metal castings from either ferrous or non-ferrous alloys. Metals are turned into parts by melting them into a liquid, pouring the metal in a mold, and removing the mold material or casting after the metal has solidified as it cools. The most common metal processed are aluminum and cast iron. However, other metals, such as steel, magnesium, copper, tin, and zinc, are also used to produce castings in foundries.

Contents

Process

In the casting process a pattern is made in the shape of the desired part. This pattern is made out of wax, wood, plastic or metal. Simple designs can be made in a single piece or solid pattern. More complex designs are made in two parts, called split patterns. A split pattern has a top or upper section, called a cope, and a bottom or lower section called a drag. Both solid and split patterns can have cores inserted to complete the final part shape. Where the cope and drag separates is called the parting line. When making a pattern it is best to taper the edges so that the pattern can be removed without breaking the mold.

The patterns are then packed in sand with a binder, which helps to harden the sand into a semi-permanent shape. Once the sand mold is cured, the pattern is removed leaving a hollow space in the sand in the shape of the desired part. The pattern is intentionally made larger than the cast part to allow for shrinkage during cooling. Sand cores can then be inserted in the mold to create holes and improve the casting's net shape. Simple patterns are normally open on top and melted metal poured into them. Two piece molds are clamped together and melted metal is then poured in to an opening, called a gate. If necessary, vent holes will be created to allow hot gases to escape during the pour. The pouring temperature of the metal should be a few hundred degrees higher than the melting point to assure good fluidity, thereby avoiding prematurely cooling, which will cause voids and porosity. When the metal cools, the sand mold is removed and the metal part is ready for secondary operations, such as machining and plating.

Advantages

The finished product of a foundry can be more geometrically complex than the product of a rolling, forging, or machining process like milling or turning. The mechanical properties of castings are equal in every direction, which makes them more suitable for multi-directional loading conditions. A foundry is the original way to produce near net shape parts. Castings frequently do not require or only require a little machining to create the finished part.

Steps

Advertisements

Melting

Melting is performed in a furnace. Virgin material, external scrap, internal scrap, and alloying elements are used to charge the furnace. Virgin material refers to commercially pure forms of the primary metal used to form a particular alloy. Alloying elements are either pure forms of an alloying element, like electrolytic nickel, or alloys of limited composition, such as ferroalloys or master alloys. External scrap is material from other forming processes such as punching, forging, or machining. Internal scrap consists of the gates, risers, or defective castings.

The process includes melting the charge, refining the melt, adjusting the melt chemistry and tapping into a transport vessel. Refining is done to remove deleterious gases and elements from the molten metal. Material is added during the melting process to bring the final chemistry within a specific range specified by industry and/or internal standards. During the tap, final chemistry adjustments are made.

Furnace

Several specialised furnaces are used to melt the metal. Furnaces are refractory lined vessels that contain the material to be melted and provide the energy to melt it. Modern furnace types include electric arc furnaces (EAF), induction furnaces, cupolas, reverberatory, and crucible furnaces. Furnace choice is dependent on the alloy system and quantities produced. For ferrous materials, EAFs, cupolas, and induction furnaces are commonly used. Reverberatory and crucible furnaces are common for producing aluminum castings.

Furnace design is a complex process, and the design can be optimized based on multiple factors. Furnaces in foundries can be any size, ranging from mere ounces to hundreds of tons, and they are designed according to the type of metals that are to be melted. Also, furnaces must be designed around the fuel being used to produce the desired temperature. For low temperature melting point alloys, such as zinc or tin, melting furnaces may reach around 327 Celsius. Electricity, propane, or natural gas are usually used for these temperatures. For high melting point alloys such as steel or nickel based alloys, the furnace must be designed for temperatures over 3600 Celsius. The fuel used to reach these high temperatures can be electricity or coke.

The majority of foundries specialize in a particular metal and have furnaces dedicated to these metals. For example, an iron foundry (for cast iron) may use a cupola, induction furnace, or EAF, while a steel foundry will use an EAF or induction furnace. Bronze or brass foundries use crucible furnaces or induction furnaces. Most aluminum foundries use either an electric resistance or gas heated crucible furnaces or reverberatory furnaces.

Mold making

Many large foundries operate their own industrial railways

Prior to pouring a casting, the foundry produces a mold. The molds are constructed by several different processes dependent upon the type of foundry, metal to be poured, quantity of parts to be produced, size of the casting and complexity of the casting. These mold processes include:

  • Sand casting - Green or resin bonded sand mold.
  • Lost-foam casting - Polystyrene pattern with a mixture of ceramic and sand mold.
  • Investment casting - Wax or similar sacrificial pattern with a ceramic mold.
  • Plaster casting - Plaster mold.
  • V-Process casting - Vacuum is used in conjunction with thermoformed plastic to form sand molds. No moisture, clay or resin is needed for sand to retain shape.
  • Die casting - Metal mold.
  • Billet (ingot) casting - Simple mold for producing ingots of metal normally for use in other foundries.

Pouring

An old geared ladle

In a foundry, molten metal is poured into molds. Pouring can be accomplished with gravity, or it may be assisted with a vacuum or pressurized gas. Many modern foundries use robots or automatic pouring machines for pouring molten metal. Traditionally, molds were poured by hand using ladles.

Shakeout

The solidified metal component is then removed from its mold. Where the mold is sand based, this can be done by shaking or tumbling. This frees the casting from the sand, which is still attached to the metal runners and gates - which are the channels through which the molten metal traveled to reach the component itself.

Degating

Degating is the removal of the heads, runners, gates, and risers from the casting. Runners, gates, and risers may be removed using cutting torches, band saws or ceramic cutoff blades. For some metal types, and with some gating system designs, the sprue, runners and gates can be removed by breaking them away from the casting with a hammer or specially designed knockout machinery. Risers must usually be removed using a cutting method (see above) but some newer methods of riser removal use knockoff machinery with special designs incorporated into the riser neck geometry that allow the riser to break off at the right place.

The gating system required to produce castings in a mold yields leftover metal, including heads, risers and sprue, sometimes collectively called sprue, that can exceed 50% of the metal required to pour a full mold. Since this metal must be remelted as salvage, the yield of a particular gating configuration becomes an important economic consideration when designing various gating schemes, to minimize the cost of excess sprue, and thus melting costs.

Surface cleaning

After degating, sand or other molding media may adhere to the casting. To remove this the surface is cleaned using a blasting process. This means a granular media will be propelled against the surface of the casting to mechanically knock away the adhering sand. The media may be blown with compressed air, or may be hurled using a shot wheel. The media strikes the casting surface at high velocity to dislodge the molding media (for example, sand, slag) from the casting surface. Numerous materials may be used as media, including steel, iron, other metal alloys, aluminum oxides, glass beads, walnut shells, baking powder or numerous other materials. The blasting media is selected to develop the color and reflectance of the cast surface. Terms used to describe this process include cleaning, blasting, shotblasting and sand blasting of castings.

Finishing

The final step in the process usually involves grinding, sanding, or machining the component in order to achieve the desired dimensional accuracies, physical shape and surface finish.

Removing the remaining gate material, called a gate stub, is usually done using a grinder or sanding. These processes are used because their material removal rates are slow enough to control the amount of material. These steps are done prior to any final machining.

After grinding, any surfaces that require tight dimensional control are machined. Many castings are machined in CNC milling centers. The reason for this is that these processes have better dimensional capability and repeatability than many casting processes. However, it is not uncommon today for many components to be used without machining.

A few foundries provide other services before shipping components to their customers. Painting components to prevent corrosion and improve visual appeal is common. Some foundries will assemble their castings into complete machines or sub-assemblies. Other foundries weld multiple castings or wrought metals together to form a finished product.

More and more the process of finishing a casting is being achieved using robotic machines like the Koyama Barinder [1]which eliminate the need for a human to physically grind or break parting lines,partings linegating material or feeders. The introduction of these machines has reduced injury to workers, costs of consumables whilst also reducing the time necessary to finish a casting. It also eliminates the problem of human error so as to increase repeatability in the quality of grinding. With a change of tooling these machines can finish a wide variety of materials including Iron, Bronze and Aluminium.

See also

References

  • Beeley, Peter (2001), Foundry Technology (2nd ed.), Oxford, UK: Butterworth-Heinemann, ISBN 978-0750645676  .
  • Campbell, John (2003), Castings (2nd ed.), Oxford, UK: Butterworth-Heinemann, ISBN 978-0750647908  .

External links


Simple English

A foundry is a place where molten (melted) metals are poured into casts, to make metal things of a certain shape.


Advertisements






Got something to say? Make a comment.
Your name
Your email address
Message