|silvery, blue cast
|Name, symbol, number||osmium, Os, 76|
|Element category||transition metal|
|Group, period, block||8, 6, d|
|Standard atomic weight||190.23 g·mol−1|
|Electron configuration||[Xe] 4f14 5d6 6s2|
|Electrons per shell||2, 8, 18, 32, 14, 2 (Image)|
|Density (near r.t.)||22.59 g·cm−3|
|Liquid density at m.p.||20 g·cm−3|
|Melting point||3306 K, 3033 °C, 5491 °F|
|Boiling point||5285 K, 5012 °C, 9054 °F|
|Heat of fusion||57.85 kJ·mol−1|
|Heat of vaporization||738 kJ·mol−1|
|Specific heat capacity||(25 °C) 24.7 J·mol−1·K−1|
|Oxidation states||8, 7, 6, 5, 4, 3, 2, 1, 0, -1, -2
(mildly acidic oxide)
|Electronegativity||2.2 (Pauling scale)|
|Ionization energies||1st: 840 kJ·mol−1|
|2nd: 1600 kJ·mol−1|
|Atomic radius||135 pm|
|Covalent radius||144±4 pm|
|Electrical resistivity||(0 °C) 81.2 nΩ·m|
|Thermal conductivity||(300 K) 87.6 W·m−1·K−1|
|Thermal expansion||(25 °C) 5.1 µm·m−1·K−1|
|Speed of sound (thin rod)||(20 °C) 4940 m/s|
|Shear modulus||222 GPa|
|Bulk modulus||462 GPa|
|Brinell hardness||3920 MPa|
|CAS registry number||7440-04-2|
|Most stable isotopes|
|Main article: Isotopes of osmium|
Osmium (pronounced /ˈɒzmiəm/, OZ-mee-əm) is a chemical element that has the symbol Os and atomic number 76. Osmium is a hard, brittle, blue-gray or blue-black transition metal in the platinum family, and is the densest natural element. Osmium is twice as dense as lead. The density of osmium is 22.61 g/cm3, slightly greater than that of iridium, the second densest element. Osmium is found in nature as an alloy, mostly in platinum ores. Osmium is also used in alloys, with platinum, iridium and other platinum group metals. Those alloys are employed in fountain pen tips, electrical contacts and in other applications where extreme durability and hardness are needed.
Osmium is an extremely dense, blue-gray, hard but brittle metal that remains lustrous even at high temperatures. Due to its hardness, brittleness, and very high melting point (the fourth highest of all elements), solid osmium is difficult to machine, form, or work. Osmium is generally considered to be the densest known element, narrowly defeating iridium. Calculations of density from the space lattice may produce the most reliable data for these elements, giving a density of 22.562±0.009 g/cm3 for iridium versus 22.587±0.009 g/cm3 for osmium. The extraordinary density of osmium is a consequence of the lanthanide contraction.
Osmium possesses quite remarkable chemical and physical properties. It has the highest melting point and the lowest vapor pressure in the platinum family. Osmium has a very low compressibility. Correspondingly, its bulk modulus is extremely high, reported between 395 and 462 GPa, which rivals that of diamond (443 GPa). However, the hardness of osmium is lower than diamond, only 4 GPa.
|Oxidation states of osmium|
Osmium forms compounds with the oxidation states ranging from −2 to +8. The most common oxidation states are +2, +3, +4, and +8. The +8 oxidation state is notable for being the highest attained by any chemical element, and aside from osmium, is encountered only in xenon and ruthenium. The oxidation state −1 and −2 represented by the two reactive compounds Na2[Os4(CO)13] and Na2[Os(CO)4] are used in the synthesis of osmium cluster compounds.
The most common compound exhibiting the +8 oxidation state is osmium tetroxide. This toxic compound is formed when powdered osmium is exposed to air, and is a very volatile, water-soluble, pale yellow, crystalline solid with a strong smell. Therefore, osmium powder has a characteristic smell of osmium tetroxide. Osmium tetroxide forms red osmates OsO4(OH)2−2 upon reaction with a base. With ammonia, it forms the nitrido-osmates OsO3N−. Osmium tetroxide boils at 130 °C and is a powerful oxidizing agent. By contrast, osmium dioxide (OsO2) is black, non-volatile, and much less reactive and toxic.
Osmium heptafluoride (OsF7) and osmium pentafluoride (OsF5) are known, but osmium trifluoride (OsF3) has not been synthesized yet. The lower oxidation states are stabilized by the larger halogens. Therefore, the trichloride, tribromide, triiodide and even osmium diiodide are known. The oxidation state +1 is only known for the osmium iodide (OsI), whereas several carbonyl complexes of osmium, such as triosmium dodecacarbonyl (Os3(CO)12), represent the oxidation state 0.
In general, the lower oxidation states of osmium are stabilized by ligands that are good σ-donors (such as amines) and π-acceptors (heterocycles containing nitrogen). The higher oxidation states are stabilized by strong σ- and π-donors, such as O2− and N3−.
Osmium has seven naturally occurring isotopes, six of which are stable: 184Os, 187Os, 188Os, 189Os, 190Os, and (most abundant) 192Os. 186Os undergoes alpha decay with such long half-life ((2.0±1.1) × 1015 years) that for practical purposes it can be considered stable. Alpha decay is predicted for all 7 naturally occurring isotopes, but due to very long half-lives, it was observed only for 186Os. It is predicted that 184Os and 192Os can undergo double beta decay but this radioactivity has not been observed yet.
187Os is the daughter of 187Re (half-life 4.56×1010 yr) and is used extensively in dating terrestrial as well as meteoric rocks (see rhenium-osmium dating). It has also been used to measure the intensity of continental weathering over geologic time and to fix minimum ages for stabilization of the mantle roots of continental cratons. This decay is a reason why rhenium-rich minerals are abnormally rich in 187Os. However, the most notable application of Os in dating has been in conjunction with iridium, to analyze the layer of shocked quartz along the K-T boundary that marks the extinction of the dinosaurs 65 million years ago.
Osmium (from Greek osme (ὀσμή) meaning "smell") was discovered in 1803 by Smithson Tennant and William Hyde Wollaston in London, England. The discovery of osmium is intertwined with that of platinum and the other metals of the platinum group. Platinum reached Europe as platina ("small silver"), first encountered in the late 17th century in silver mines around the Chocó Department, in Colombia. The discovery that this metal was not an alloy, but a distinct new element, was published in 1748. Chemists who studied platinum dissolved it in aqua regia (a mixture of hydrochloric and nitric acids) to create soluble salts. They always observed a small amount of a dark, insoluble residue. Joseph Louis Proust thought that the residue was graphite. Victor Collet-Descotils, Antoine François, comte de Fourcroy, and Louis Nicolas Vauquelin also observed the black residue in 1803, but did not obtain enough material for further experiments.
In 1803, Smithson Tennant analyzed the insoluble residue and concluded that it must contain a new metal. Vauquelin treated the powder alternately with alkali and acids and obtained a volatile new oxide, which he believed to be of this new metal—which he named ptene, from the Greek word πτηνος (ptènos) for winged. However, Tennant, who had the advantage of a much larger amount of residue, continued his research and identified two previously undiscovered elements in the black residue, iridium and osmium. He obtained a yellow solution (probably of cis–[Os(OH)2O4]2−) by reactions with sodium hydroxide at red heat. After acidification he was able to distill the formed OsO4. He named osmium after Greek osme meaning "a smell", because of the smell of the volatile osmium tetroxide. Discovery of the new elements was documented in a letter to the Royal Society on June 21, 1804.
Uranium and osmium were early successful catalysts in the Haber process, the nitrogen fixation reaction of nitrogen and hydrogen to produce ammonia, giving enough yield to make the process economically successful. However, in 1908 cheaper catalysts based on iron and iron oxides were introduced for the first pilot plants.
Osmium is one of the least abundant elements in the Earth's crust with an average mass fraction of 0.05 ppb in the continental crust. Osmium is found in nature as an uncombined element or in natural alloys; especially the iridium–osmium alloys, osmiridium (osmium rich), and iridiosmium (iridium rich). In the nickel and copper deposits, the platinum group metals occur as sulfides (i.e. (Pt,Pd)S)), tellurides (e.g. PtBiTe), antimonides (e.g. PdSb), and arsenides (e.g. PtAs2); in all these compounds platinum is exchanged by a small amount of iridium and osmium. As with all of the platinum group metals, osmium can be found naturally in alloys with nickel or copper.
Within the Earth's crust, osmium, like iridium, is found at highest concentrations in three types of geologic structure: igneous deposits (crustal intrusions from below), impact craters, and deposits reworked from one of the former structures. The largest known primary reserves are in the Bushveld igneous complex in South Africa, though the large copper–nickel deposits near Norilsk in Russia, and the Sudbury Basin in Canada are also significant sources of osmium. Smaller reserves can be found in the United States. The alluvial deposits used by pre-Columbian people in the Chocó Department, Colombia are still a source for platinum group metals. The second large alluvial deposit was found in the Ural Mountains, Russia, which is still mined.
Osmium is obtained commercially as a by-product from nickel and copper mining and processing. During electrorefining of copper and nickel, noble metals such as silver, gold and the platinum group metals, together with non-metallic elements such as selenium and tellurium settle to the bottom of the cell as anode mud, which forms the starting material for their extraction. In order to separate the metals, they must first be brought into solution. Several methods are available depending on the separation process and the composition of the mixture; two representative methods are fusion with sodium peroxide followed by dissolution in aqua regia, and dissolution in a mixture of chlorine with hydrochloric acid. Osmium, ruthenium, rhodium and iridium can be separated from platinum, gold and base metals by their insolubility in aqua regia, leaving a solid residue. Rhodium can be separated from the residue by treatment with molten sodium bisulfate. The insoluble residue, containing Ru, Os and Ir, is treated with sodium oxide, in which Ir is insoluble, producing water-soluble Ru and Os salts. After oxidation to the volatile oxides, RuO4 is separated from OsO4 by precipitation of (NH4)3RuCl6 with ammonium chloride.
After it is dissolved, osmium is separated from the other platinum group metals by distillation or extraction with organic solvents of the volatile osmium tetroxide. The first method is similar to the procedure used by Tennant and Wollaston. Both methods are suitable for industrial scale production. In either case, the product is reduced using hydrogen, yielding the metal as a powder or sponge that can be treated using powder metallurgy techniques.
Neither the producers nor the United States Geological Survey published any production amounts for osmium. Estimations of the United States consumption date published from 1971, which gives a consumption in the United States of 2000 troy ounces (62 kg), would suggest that the production is still less than 1 ton per year.
Because of the volatility and extreme toxicity of its oxide, osmium is rarely used in its pure state, and is instead often alloyed with other metals. Those alloys are utilized in high-wear applications. Osmium alloys such as osmiridium are very hard and, along with other platinum group metals, are used in the tips of fountain pens, instrument pivots, and electrical contacts, as they can resist wear from frequent operation. The stylus (needle) in early phonograph designs was also made of osmium, especially for 78-rpm records, until sapphire and synthetic diamond replaced the metal in later designs for 45-rpm and 33-rpm long-playing records.
Osmium tetroxide has been used in fingerprint detection and in staining fatty tissue for optical and electron microscopy. As a strong oxidant, it cross-links lipids mainly by reacting with unsaturated carbon-carbon bonds, and thereby both fixes biological membranes in place in tissue samples and simultaneously stains them. Because osmium atoms are extremely electron dense, osmium staining greatly enhances image contrast in transmission electron microscopy (TEM) studies of biological materials. Those carbon materials have otherwise very weak TEM contrast (see image). Another osmium compound, osmium ferricyanide (OsFeCN), exhibits similar fixing and staining action.
The tetroxide and a related compound, potassium osmate, are important oxidants for chemical synthesis, despite being very poisonous. For the Sharpless asymmetric dihydroxylation, which uses osmate for the conversion of a double bond into a vicinal diol, Karl Barry Sharpless won the Nobel Prize in Chemistry in 2001.
In 1898 an Austrian chemist, Auer von Welsbach, developed the Oslamp with a filament made of osmium, which he introduced commercially in 1902. After only few years, osmium was replaced by the more stable metal tungsten (also known as wolfram). Tungsten has the highest melting point of any metal, and using it in light bulbs increases the luminous efficacy and life of incandescent lamps.
The light bulb manufacturer OSRAM (founded in 1906 when three German companies, Auer-Gesellschaft, AEG and Siemens & Halske, combined their lamp production facilities) derived its name from the elements of OSmium and wolfRAM.
Like palladium, powdered osmium effectively absorbs hydrogen atoms. This could make osmium a potential candidate for a metal hydride battery electrode. However, osmium is expensive and would react with potassium hydroxide, the most common battery electrolyte.
Osmium has high reflectivity in the ultraviolet range of the electromagnetic spectrum; for example, at 600 Å osmium has a reflectivity two times that of gold. This high reflectivity is desirable in space-based UV spectrometers which have reduced mirror sizes due to space limitations. Osmium-coated mirrors were flown in several space missions aboard the Space Shuttle, but it soon became clear that the oxygen radicals in the low earth orbit are abundant enough to significantly deteriorate the osmium layer.
Finely divided metallic osmium is pyrophoric. Osmium reacts with oxygen at room temperature forming volatile osmium tetroxide. Some osmium compounds are also converted to the tetroxide if oxygen is present. This makes osmium tetroxide the main source for the contact to the environment. Osmium tetroxide is highly volatile and penetrates skin readily, and is very toxic by inhalation, ingestion, and skin contact. Airborne low concentrations of osmium tetroxide vapor can cause lung congestion and skin or eye damage, and should therefore be used in a fume hood. Osmium tetroxide is rapidly reduced to relatively inert compounds by polyunsaturated vegetable oils, such as corn oil.
(There is currently no text in this page)
There is not much osmium on earth. There is actually such a small amount that osmium is very expensive.
Osmium is a metal and it does not react very much, and such a metal is known as a "noble metal".