# Superconducting magnet: Wikis

Note: Many of our articles have direct quotes from sources you can cite, within the Wikipedia article! This article doesn't yet, but we're working on it! See more info or our list of citable articles.

# Encyclopedia

A superconducting magnet is an electromagnet that is built using coils of superconducting wire. They must be cooled to cryogenic temperatures during operation. Their advantages are that they can produce stronger magnetic fields than ordinary iron-core electromagnets, and can be cheaper to operate, since no power is lost to ohmic resistance in the windings.

Schematic of a 20 tesla superconducting magnet with vertical bore

## Construction

### Cooling

During operation, the magnet windings must be cooled below their critical temperature; the temperature at which the winding material changes from the normal resistive state and becomes a superconductor. Liquid helium is used as a coolant for most superconductive windings, even those with critical temperatures far above its boiling point of 4.2 K. This is because the lower the temperature, the better superconductive windings work - the higher the currents and magnetic fields they can stand without returning to their nonsuperconductive state. The magnet and coolant are contained in a thermally insulated container (dewar) called a cryostat. To keep the helium from boiling away, the cryostat is usually constructed with an outer jacket containing (significantly cheaper) liquid nitrogen at 77 K. One of the goals of the search for high temperature superconductors is to build magnets that can be cooled by liquid nitrogen alone. At temperatures above about 20 K cooling can be achieved without boiling off cryogenic liquids.[citation needed]

### Materials

The maximum magnetic field achievable in a superconducting magnet is limited by the field at which the winding material ceases to be superconducting, its 'critical field', Hc, which for type-II superconductors is its upper critical field. Another limiting factor is the 'critical current', Ic at which the winding material also ceases to be superconducting. Advances in magnets have focused on creating better winding materials.

The superconducting portions of most current magnets are composed of niobium-titanium.[1] This material has critical temperature of 10 kelvins and can superconduct at up to about 15 teslas. More expensive magnets can be made of niobium-tin (Nb3Sn). These have a Tc of 18 K. When operating at 4.2 K they are able to withstand a much higher magnetic field intensity, up to 25 to 30 teslas. Unfortunately, it is far more difficult to make the required filaments from this material. This is why sometimes a combination of Nb3Sn for the high field sections and Nb3Ti for the lower field sections is used.

High temperature superconductors (eg. BSCCO or YBCO) may be used for high-field inserts when magnetic fields are required which are higher than Nb3Sn can manage.[citation needed] BSCCO, YBCO or magnesium diboride may also be used for current leads, conducting high currents from room temperature into the cold magnet without an accompanying large heat leak from resistive leads.[citation needed]

### Coil windings

The coil windings of a superconducting magnet are made of wires or tapes of Type II superconductors (e.g.niobium-titanium or niobium-tin). The wire or tape itself may be made of tiny filaments (about 20 micrometers thick) of superconductor in a copper matrix. The copper is needed to add mechanical stability, and to provide a low resistance path for the large currents in case the temperature rises above Tc or the current rises above Ic and superconductivity is lost. These filaments need to be this small because in this type of superconductor the current only flows skin-deep.[citation needed] The coil must be carefully designed to withstand (or counteract) magnetic pressure and Lorentz forces that could otherwise cause wire fracture or crushing of insulation between adjacent turns.

## Operation

7 T horizontal bore superconducting magnet, part of a mass spectrometer. The magnet itself is inside the cylindrical cryostat.

### Power supply

The current to the coil windings is provided by a high current, very low voltage DC power supply, since in steady state the only voltage across the magnet is due to the resistance of the feeder wires. Any change to the current through the magnet must be done very slowly, first because electrically the magnet is a large inductor and an abrupt current change will result in a large voltage spike across the windings, and more importantly because fast changes in current can cause eddy currents and mechanical stresses in the windings that can precipitate a quench (see below). So the power supply is usually microprocessor-controlled, programmed to accomplish current changes gradually, in gentle ramps. It usually takes several minutes to energize or deenergize a laboratory sized magnet.

### Persistent mode

An alternate operating mode, once the magnet has been energized, is to short-circuit the windings with a piece of superconductor. The windings become a closed superconducting loop, the power supply can be turned off, and persistent currents will flow for months, preserving the magnetic field. The advantage of this persistent mode is that stability of the magnetic field is better than is achievable with the best power supplies, and no energy is needed to power the windings. The short circuit is made by a 'persistent switch', a piece of superconductor inside the magnet connected across the winding ends, attached to a small heater. In normal mode, the switch wire is heated above its transition temperature, so it is resistive. Since the winding itself has no resistance, no current flows through the switch wire. To go to persistent mode, the current is adjusted until the desired magnetic field is obtained, then the heater is turned off. The persistent switch cools to its superconducting temperature, short circuiting the windings. The current and the magnetic field will not actually persist forever, but will decay slowly according to a normal L/R time constant:

$H = H_0 e^{-(R/L)t}\,$

where $R\,$ is a small residual resistance in the superconducting windings due to joints or a phenomenon called flux motion resistance. Nearly all commercial superconducting magnets are equipped with persistent switches.

### Magnet quench

A quench is an abnormal termination of magnet operation that occurs when part of the superconducting coil enters the normal (resistive) state. This can be because the field inside the magnet is too large, the rate of change of field is too large (causing eddy currents and resultant heating in the copper support matrix), or a combination of the two. More rarely a defect in the magnet can cause a quench. When this happens, that particular spot is subject to rapid Joule heating, which raises the temperature of the surrounding regions. This pushes these into the normal state as well, which leads to more heating in a chain reaction. The entire magnet rapidly becomes normal (this can take several seconds, depending on the size of the superconducting coil). This is accompanied by a loud bang as the energy in the magnetic field is converted to heat, and rapid boil-off of the cryogenic fluid. The abrupt decrease of current can result in kilovolt inductive voltage spikes and arcing. Permanent damage to the magnet is rare, but components can be damaged by localised heating or large mechanical forces. Practical magnets usually have safety devices to remove the current or limit it when the beginning of a quench is detected. If a large magnet undergoes a quench, the inert vapor formed by the evaporating cryogenic fluid can present a significant asphyxiation hazard to operators by displacing breathable air. A large section of the superconducting magnets in CERN's Large Hadron Collider unexpectedly quenched during start-up operations in 2008, necessitating a replacement of a number of magnets.[2]

## History

Although the idea of making electromagnets with superconducting wire was proposed by Heike Kamerlingh Onnes shortly after he discovered superconductivity in 1911, a practical superconducting electromagnet had to await the discovery of type-II superconductors that could stand high magnetic fields. The first successful superconducting magnet was built by George Yntema in 1954 using niobium wire and achieved a field of 0.71 T at 4.2 K.[3] Widespread interest was sparked by Kunzler's 1961 discovery of the advantages of niobium-tin as a high Hc, high current winding material.[4]

In 1986, the discovery of high temperature superconductors by Georg Bednorz and Karl Muller energized the field, raising the possibility of magnets that could by cooled by liquid nitrogen instead of the more difficult to work with helium.

In 2007 a magnet with windings of YBCO achieved a world record field of 26.8 teslas.[5] The US National Research Council has a goal of creating a 30 tesla superconducting magnet.

## Uses

An MRI machine that uses a superconducting magnet. The magnet is inside the doughnut-shaped housing, and can create a 3 tesla field inside the central hole.

Superconducting magnets have a number of advantages over resistive electromagnets. They can achieve an order of magnitude stronger field than ordinary ferromagnetic-core electromagnets, which are limited to fields of around 2 T. The field is generally more stable, resulting in less noisy measurements. They can be smaller, and the area at the center of the magnet where the field is created is empty rather than being occupied by an iron core. Most importantly, for large magnets they can consume much less power. In the persistent state (above), the only power the magnet consumes is that needed for any refrigeration equipment to preserve the cryogenic temperature. Higher fields, however can be achieved with special cooled resistive electromagnets, as superconducting coils will enter the normal (non-superconducting) state (see quench, above) at high fields.

Superconducting magnets are widely used in MRI machines, NMR equipment, mass spectrometers, magnetic separation processes, and particle accelerators.

One of the most challenging use of SC magnets is in the LHC particle accelerator [6]. The niobium-titanium (Nb-Ti) magnets will operate at 1.9 K to allow them to run safely at 8.3 T. Each magnet will store 7 MJ. In total the magnets will store 10.4 GJ. Once or twice a day, as the protons are accelerated from 450 GeV to 7 TeV, the field of the superconducting bending magnets will be increased from 0.54 T to 8.3 T.

The central solenoid and toroidal field superconducting magnets designed for the ITER fusion reactor use niobium-tin (Nb3Sn) as a superconductor. The Central Solenoid coil will carry 46 kA and produce a field of 13.5 teslas. The 18 Toroidal Field coils at max field of 11.8 T will store 41 GJ (total?). They have been tested at a record 80 kA. Other lower field ITER magnets (PF and CC) will use niobium-titanium. Most of the ITER magnets will have their field varied many times per hour.

## References

1. ^ "Characteristics of Superconducting Magnets". Superconductivity Basics. American Magnetics Inc. website. 2008. Retrieved 2008-10-11.
2. ^
3. ^ Yntema, G.B. (1955). "Superconducting winding for electromagnets". Physics Review (APS) 98: 1197.
4. ^ Kunzler, J.E.; E. Buehler, F.S.L. Hsu, J.H. Wernick (1961). "Superconductivity in Nb3Sn at high current density in a magnetic field of 88 kilogauss". Physics Review Letters (APS) 6: 890.
5. ^ "New mag lab record promises more to come". News Release. National High Magnetic Field Laboratory, USA. August 7, 2007. Retrieved 2008-10-23.
6. ^ http://irfu.cea.fr/Phocea/file.php?class=std&file=Seminaires/1595/Dapnia-Nov07-partB.ppt Operational challenges of the LHC

• Martin N. Wilson, Superconducting Magnets (Monographs on Cryogenics), Oxford University Press, New edition (1987), ISBN 978-0-19-854810-2.
• Yukikazu Iwasa, Case Studies in Superconducting Magnets: Design and Operational Issues (Selected Topics in Superconductivity), Kluwer Academic / Plenum Publishers, (Oct 1994), ISBN 978-0-306-44881-2.
• Habibo Brechna, Superconducting magnet systems, New York, Springer-Verlag New York, Inc., 1973, ISBN 3-540-06103-7, ISBN 0-387-06103-7